Facile modifications of polyimide via chloromethylation: II. Synthesis and characterization of thermocurable transparent polyimide having methylene acrylate side groups

From chloromethylated polyimide, a useful starting material for modification of aromatic polyimides, a thermocurable transparent polyimide having acrylate side groups was prepared. In the presence of 1,8‐diazabicyclo[5,4,0]undec‐7‐ene, chloromethylated polyimide was esterified with acrylic acid to synthesize poly(imide methylene acrylate). The polymer was soluble in organic solvent, which makes it possible to prepare a planar film by spin coating. The polymer film became insoluble after thermal treatment at 230 °C for 30 min. Optical transparency of the film at 400 nm (for 1 µm thickness) was higher than 98 % and not affected by further heating at 230 °C for 250 min. Adhesion properties measured by the ASTM D3359‐B method ranged from 4B to 5B. Preliminary results of planarization testing showed a high degree of planarization (DOP) value (>0.53). These properties demonstrate that poly(imide methylene acrylate) could be utilized as a thermocurable transparent material in fabricating display devices such as TFT‐LCD. Copyright © 2004 Society of Chemical Industry     

Preparation of flexible polyhedral particles via concentrated emulsion templating polymerization

This paper presents recent efforts on the preparation of flexible polyhedral particles via concentrated emulsion templating polymerization in which the hydrophilic monomer (acrylamide) and hydrophobic monomer (butyl acrylate) are polymerized simultaneously in the continuous and dispersed phase, respectively. Such templating polymerization has been enhanced in our systems owing to the introduction of acrylamide monomer and their higher polymerization rate in continuous phase as compared with butyl acrylate in dispersed phase. Diffusion between the different phases was also inhibited. Furthermore, the stability of the concentrated emulsion and the molecular weight of the produced poly(butyl acrylate) were found to be significantly affected by the amount of redox initiator. The morphology of the particles could be controlled by varying the volume fraction of the dispersed phase and the polyhedral particles were achieved at higher volume fraction. Copyright © 2005 Society of Chemical Industry     

温度敏感葡聚糖凝胶的合成及其细胞相容性研究

合成了N-异丙基丙烯酰胺（NIPAAm）与葡聚糖的共聚水凝胶，利用红外光谱表征了单体和凝胶结构，研究了水凝胶在去离子水和细胞培养基中的温度响应性，并对凝胶进行了细胞培养和脱附研究．结果表明，共聚凝胶具有很好的温度敏感性和细胞相容性，可以通过控制温度变化，实现对细胞的无损伤脱附．     

QFT control design for an approximately linearized pneumatic positioning system

A block‐oriented approximate feedback linearization for control of a pneumatic cylinder positioning system is introduced and a rather detailed discussion is presented on the uncertain linearization residual characterization. It is shown that making use of the characterized gain–phase information of the linearized system leads to a more reasonable trade‐off between performance and stability in the QFT control design and thus results in high control performance. Simulation and experimental results are shown. Copyright © 2003 John Wiley & Sons, Ltd.     

In situ formation of multi scale reinforcing phases to improve performance of Al2O3-SiC C castables

In order to improve the physical properties and slag corrosion resistance of refractory materials for hot metal pretreatment, different contents of composite metal powders (CMP) were introduced into Al2O3-SiC-C refractory castables. The effect of CMP on the microstructure, physical properties and slag corrosion resistance of Al2O3-SiC-C refractory castables were studied. The results show that the multi scale reinforcing phases including flake crystals, rod shaped fibers, filamentous fibers and whiskers are in situ formed in the samples with addition of CMP, which result to the improvement of the cold modulus of rupture and cold crushing strength. When the addition of CMP is 6 wt.%, the high temperature modulus of rupture increases by 231%, the thermal shock resistance increases by 77% after thermal shock by water cooling 5 times and the percentage of the slag resistant area reduces by 37.2%.     

Asset-Management of Transformers Based on Condition Monitoring and Standard Diagnosis [Feature Article]

In this paper, a methodology is developed to use data acquisition derived from condition monitoring and standard diagnosis for rehabilitation purposes of transformers. The interpretation and understanding of the test data are obtained from international test standards to determine the current condition of transformers. In an attempt to ascertain monitoring priorities, the effective test methods are selected for transformer diagnosis. In particular, the standardization of diagnostic and analytical techniques are being improved that will enable field personnel to more easily use the test results and will reduce the need for interpretation by experts. In addition, the advanced method has the potential to reduce the time greatly and increase the accuracy of diagnostics. The important aim of the standardization is to develop the multiple diagnostic models that combine results from the different tests and give an overall assessment of reliability and maintenance for transformers.     

利用铝（100）面隧道孔制备纳米模板及有序阵列材料

高纯铝箔通常通过电化学扩面后用作铝电解电容器的阳极材料。利用铝箔（100）面隧道孔制备纳米模板。这种纳米模板的特点是制作简单、模板面积大，纳米阵列材料形状可控性强。还利用两步电化学侵蚀铝箔的特殊工艺，研制出纵横交错的TiO2纳米有序阵列材料。     

择形催化合成2,6-DMN的研究进展

介绍了2,6-二甲基萘(2,6-DMN)的制备方法,详细论述了萘、甲基萘在分子筛催化剂上择形催化合成2,6-DMN的研究进展,提出了择形催化合成2,6-DMN的研究方向。     

有粘结预应力在252m地下室顶板中的应用

在总长度 2 5 2m的超长不设缝地下室顶板中 ,采用了预应力、设置后浇带等综合抗裂技术 ,并对有粘结预应力平板的设计理论、施工工艺、锚固体系及超长结构预应力损失控制和抗裂控制作了深入研究。     

IF钢冷轧及再结晶初期微观组织的TEM研究

采用透射电子显微镜对不同压下量和再结晶初期的IF钢样品进行了研究．结果表明：无论是在较小形变量下还是在较大形变量下，形变不均匀性是普遍存在的；冷变形程度不同，织构组分不同，TEM形貌也不同；在再结晶的最初期，冷轧的形变组织演变为近乎等轴的亚晶，优先形成{111}〈uvw〉取向的晶核，晶核逐渐吞并周围的形变基体而长大，最终形成再结晶γ-纤维织构．